POSTECH Solves the Durability Issue of Hydrogen Cars
[Professor Yong-Tae Kim’s research team improves the durability of automotive fuel cells through selective electro-catalysis.]
When a bicycle gets wet in the rain, the frame and chain become corroded or rusty which shorten the life of the bike. Oil needs to be regularly applied to prevent this from happening. Battery cells are devices that create electrical energy through moving electrons by triggering oxidation and reduction reactions*1 separately. But they also corrode when exposed to oxygen. Can these cells also be greased to prevent rusting?
A research team led by Professor Yong-Tae Kim and doctoral student Sang Moon Jung of Materials Science and Engineering at POSTECH used a catalyst (Pt/HxWO3) that combines platinum and hydrogen tungsten bronze to solve the corrosion in fuel cells that occur when hydrogen cars are shut down. The catalyst, recently introduced in Nature Catalysis – a sister journal of Nature – has been shown to promote hydrogen oxidation and selectively suppress oxygen reduction reactions (ORR).
As eco-friendly hydrogen cars become more common, the race for research and development for improving fuel cell performance – the heart of hydrogen cars – is getting fierce around the world. The performance of automotive fuel cells are severely low owing to their intermittent shut-downs compared to power-generating fuel cells that do not stop once started. This is because when ignition is turned off, the ORR occurs as air is temporarily introduced into the anode*2, and corrosion of the cathodic components accelerates as the potential of cathod*3 surges instantaneously.
The research team focused on the Metal Insulator Transition (MIT) phenomenon*4, which can selectively change the conductivity of materials depending on the surrounding environment, to solve the problem of durability degradation in automotive fuel cells.
In particular, the research team focused on the tungsten oxide (WO3) that has traditionally been used as an electrical discoloration material since it greatly changes conductivity via the insertion and reduction of protons*5. Applying the MIT phenomenon of WO3 in normal operation results in an electrode reaction while maintaining the H-WO3 (conductor) state with the insertion of a proton. In contrast, when ignition is shut-down, mixed air is drawn in which increases the oxygen pressure and changes it into WO3 (subconductor) which stops the electrode reaction, thus solving the issue of cathodic corrosion.
The Pt/HxWO3 selective hydrogen oxidation reaction (HOR) catalysts imparted by the metal-insulator transition phenomenon showed more than twice the durability of conventional commercial Pt/C catalyst materials in shut-down conditions in the MEA evaluation*6 of automotive fuel cells.
Professor Yong-Tae Kim who led the research commented, “This research has dramatically improved the durability of automotive fuel cells.” He added, “It is anticipated that the commercialization of hydrogen cars may be further facilitated through these findings.”
This research was conducted with the support from the Future Materials Discovery Project and the hydrogen energy innovation technology development program of the Ministry of Science and ICT.
1. oxidization-reduction reaction
Electron transmission between materials causes oxidation and reduction at the same time. The oxidation number for the side that loses the electron increases and the side that gains an electron decreases in oxidation number.
2. Anode
Generally, the electrode on the side where an electron flows out due to an oxidation reaction that loses electrons.
3. Cathode
The electrode on the side where the electron flows in due to the reduction reaction of the electron.
4. Metal Insulator Transition (MIT) phenomenon
Refers to a phenomenon in which a subconductor material suddenly transitions from an insulator (semiconductor characteristic) to metal due to changes in temperature, electric field or external environmental factors (gas levels). In this study, the subconductor shows insulator characteristics when oxygen pressure is high and metal characteristics when hydrogen pressure is high.
5. Insertion and reduction
The insertion of a proton is a phenomenon in which the proton enters the interior of the tungsten oxide (WO3) electrode material, and the reduction of a proton is a phenomenon in which the proton exits the tungsten oxide electrode material.
6. MEA Evaluation
MEA is an abbreviation for Membrane Electrode Assembly, which refers to an aggregation of electrolytic membranes, anode electrodes and cathodic poles. This refers to the characteristic evaluation of these MEAs.